M-CORR 600 – Rubberised Corrosion Resistant Coating

• All surfaces should be cleaned appropriately and must be free from mould, moss, algae, dust and debris.
• The surface of the roof must be pressure washed at a minimum 2000psi and then dried off using squeegees or allowed to dry overnight.
  • Concrete and porous surfaces – All surfaces must be primed using M-CHEM 100 applied at a wet film thickness of 150 microns.
  • Plywood and wooden surfaces – All surfaces must be primed using M-CHEM 100 a low viscosity epoxy primer applied at a wet film thickness of 150 microns.
  • Metal surfaces – All surfaces must be primed using M-CORR 200 a low viscosity solvent based epoxy primer applied at a wet film thickness of 150 microns.
  • Bituminous, Asphalt or Mineral Felt surfaces – All surfaces must be primed using an appropriate low viscosity solvent based acrylic primer at a wet film thickness of 100 microns.

Prior to mixing please ensure the following:

• The base component is at a temperature between 15-25°C.
• Do not apply the material when the ambient or substrate temperature is below 5°C.

• M-CORR 600 is a single component material.
• Using a low speed electric paddle mixer ensure you have a consistent mix of acrylic emulsion.
• Once mixing is complete use the mixed paste as soon possible after mixing.

Brush & Roller

• Apply the 1st coat of material using a medium pile roller at a wet film thickness of 750 microns.
• While the coating is still wet lay 100gm glass fibre chop strand matting onto the surface.
• Back roll a thin layer of 554 RB membrane onto the surface to ensure the matting is fully encapsulated.
• Allow to cure for approximately 8 hours (20°C).
• Apply a 2nd coat at a wet film thickness of 750 microns.