Description
M-RUBBER 101 – Multi Surface Rubber Primer
This single component, easy to use, solvent free abrasion resistant urethane elastomer has been specifically developed as an abrasion resistant lining for repairs to a wide range of rubber surfaces such as nitrile, neoprene & natural rubber.
Typical Uses
- Used as sealer for Gaskets
- Lining of process equipment such as chutes, hoppers fans and pumps
Please contact us to discuss your project before purchasing this material to confirm suitability.
Application Guide
- All oil and grease must be removed from the surface using an appropriate cleaner such as MEK or similar type solvent.
- All surfaces must be abrasive blasted to ISO 8501/4 Standard SA2.5 (SSPC SP10/ NACE 2) minimum blast profile of 75 microns using an angular.
- Once blast cleaned the surface must be degreased and cleaned using MEK or similar type solvent.
- All oil and grease must be removed from the surface using an appropriate cleaner such as MEK.
- All surfaces must be mechanically abraded using handheld grinders to ISO 8501/4 ST3 (SSPC SP3 ST3).
- Once abraded, the surface must be degreased and cleaned using MEK or similar type material.
PLEASE NOTE: Soluble salt contaminated surfaces the substrate must be pressure washed with clean water and checked for salt contamination this process may need to be repeated several times.,
- Remove any surface contamination and degrease with MEK.
- Use a suitable carding tool or MBX bristle blaster to roughen the surface before brushing away any debris.
- Once all surfaces, metallic or rubber have been prepared, apply a Multi-surface Primer to all surfaces with a stippling action avoiding ponding. Leave to cure until touch dry and for a minimum of 20 minutes at 20°C (68°F).
Prior to mixing please ensure the following:
- The base component is at a temperature between 15-25°C.
- Do not apply the material when the ambient or substrate temperature is below 5°C.
- M-RUBBER 101 is supplied as a single component liquid, shake well before use.
| Appearance | Base Activator Mixed | Black paste Amber paste Black paste |
| Mixing Ratio | By Weight By Volume | 100:26 100:23 |
| Density | Base Activator Mixed | 1.05 1.15 1.08 |
| Solids Content | 100% | |
| Sag Resistance | Nil at | 2.5 cm |
| Usable Life | 10°C 20°C 30°C | 15 minutes 9 minutes 4 minutes |
| Coverage | 500g will cover 0.46m² at a nominal thickness of 1mm (not allowing for losses) |
|
| Cure Times at 20°C | Minimum overcoating time Maximum overcoating time Light dry Heavy load Water/ sea water immersion | 30 hours 36 hours 8 days 24 hours 3 days |
| Storage Life | Unopened and stored in dry conditions (15-30°C) | 1 year |
| Tensile Strength | Tested to BS EN ISO 37 | 100 kg/cm² (1450psi) |
| Tear Strength | Tested to BS EN ISO 34 | 4690kg/m (262pli) |
| Elongation | Tested to BS EN ISO 37 | 900% |
| Shore A Hardness | Tested to BS EN ISO 868 | 85 |
| Linear Shrinkage | 500x 50x 10mm <0.05% | |
| 90 degree Peel Adhesion to Steel | Tested to ASTM D429 (Abrasive blasted and primed) | 3132 kg/m (175pli) |
| 180 degree Peel Adhesion to Rubbers | Tested to ASTM D413 (toughened and primed) | Neoprene 609 kg/m 34 pli (TF) Nitrile 377 kg/m 21 pli (CS) Natural 215 kg/m 12 pli (CS) EPDM 428 kg/m 24 pli (CS) TF = Tape failure CS = Cohesive failure in substrate |
| Los Angeles Abrasion | Test (modified) After 7 days cure at 20 ̊ C using granite and 150# silicon carbide. | Volume loss per week 0.92% |
| Dielectric Strength | Tested to ASTM D149 | 16KV/mm |
| Heat Resistance | Suitable for long term water immersion at temperatures up to 50°C and intermittent contact water contact up to 80°. Resistant to dry heat up to 120°C |
|
| Chemical Resistance , | The product resists attack by a wide variety of inorganic acids | alkalis salts organic media |
M-CERAMIC 402 - Epoxy Ceramic Wear Compound - High Abrasion & Impact