M-PRIME 100 – Low Viscosity Epoxy Concrete Primer

M-PRIME 100 - Low Viscosity Epoxy Concrete Primer

£44.50£538.46 Excl VAT

M-PRIME 100 – Low Viscosity Epoxy Concrete Primer

£44.50£538.46 Excl VAT

Is a solvent-free clear epoxy primer, which provides outstanding penetration into concrete and other cementitious substrates and helps to consolidate weak surfaces. Ideal for priming concrete floors, bunds and other concrete structures before the application of other MaxKote coatings of lining systems.

 

Description

M-PRIME 100 – Epoxy Concrete Primer Sealer

M-PRIME 100 -Epoxy concrete primer sealer, is a solvent-free, clear epoxy primer, which provides outstanding penetration into concrete and other cementitious substrates and helps to consolidate weak surfaces.

Ideally used in conjunction  with other MaxKote lining or coating systems

Once mixed the product  is used for priming concrete floors, bunds and concrete structures with a moisture content below 8%.

Typical Uses

  • Concrete structures
  • Concrete storage tanks
  • Bunds and containment areas
  • Floor areas

Please contact us to discuss your project before purchasing this material to confirm suitability.

Application Guide

Existing Concrete

  • Remove any contamination and lightly abrasive blast or scarify taking care not to expose the aggregate.

New Concrete

  • Allow new concrete to cure for a minimum 21 days and remove any surface laitance before coating.
  • Ensure the moisture content of the concrete is 8% or below.
  • Suitable for application where the surface temperature is 5°C (40°F) or above

Prior to mixing please ensure the following:

  • The base component is at a temperature between 15-25°C.
  • Do not apply the material when the ambient or substrate temperature is below 5°C.
  • Mix the base component (amber liquid) with the activator component (amber liquid) in full units as supplied, ideally use slow speed paddle mixer.

  • For small quantities us a mixing ratio of: 2:1 by volume or 2.25:1 by weight.

  • When mixing both materials it is essential to have a uniform clear fluid that is streak free.

  • Once mixed, the material should be used within 40-45 minutes at 20°C.

  • To ensure best results use the mixed fluid as soon possible after mixing.

Brush & Roller

  • Pour the mixed material into a paint kettle or paint tray (this will maximise the usable life).
  • Using a 50mm (2”) wide synthetic brush, stripe coat all edges, joints, corners and equipment with the mixed material.
  • The stripe coat must be approximately 100mm (4”) wide, at 150 microns (6mil) wet film thickness.
  • Once the stripe coat has cured sufficiently and is capable of being overcoated, apply the mixed product to all surfaces at 150 microns (6mil) wet film thickness.
AppearanceBase
Activator
Mixed

Low viscosity pale straw liquid
Amber liquid
Low viscosity pale straw liquid
Mixing RatioBy Weight
By Volume
2.24:1
2:1
DensityBase
Activator
Mixed
1.12
1.00
1.08
Solids Content100%
Sag ResistanceNil at150 microns
Usable Life10°C
20°C
30°C

50 minutes
25 minutes
12.5 minutes

Coverage At 150 microns the theoretical coverage rate is

6.66m² per ltr
Cure Times at 20°C Minimum overcoating time
Maximum overcoating time
3 hours
36 hours
Storage LifeUnopened and stored in dry conditions (15-30°C)5 years
Pull off adhesion Elcometer pull off adhesion testerDry 525psi
37kg/cm² (cohesive in substrate)
Wet 475psi
33.4 kg/cm² (cohesive in substrate)
Compressive StrengthTested to ASTM D 695629kg/cm² (8945psi)
Flexural StrengthTested to ASTM D790371kg/cm² (5275psi)
HardnessShore D to ASTM D224084
Heat ResistanceSuitable for use in immersed conditions at temperatures up to:
Suitable for use in dry conditions at temperatures up to dependant on load:
60°C
150°C

Additional information

Weight 4.5 kg
Unit Size

18ltr, 1ltr, 4ltr

Colour

Clear